A Ruby is a pink to blood-red gemstone, a variety of the mineral corundum (aluminium oxide). The common red color is caused mainly by the presence of the element chromium. Its name comes from ruber, Latin for red. Other varieties of gem-quality corundum are called sapphires. The ruby is considered one of the four precious stones, together with the sapphire, the emerald and the diamond.

Prices of rubies are primarily determined by color. The brightest and best "red" called pigeon blood-red, commands a huge premium over other rubies of similar quality. After color follows clarity: similar to diamonds, a clear stone will command a premium, but a ruby without any needle-like rutile inclusions will indicate that the stone has been treated one way or another. Cut and carat (size) also determine the price.

Physical Properties

Rubies have a hardness of 9.0 on the Mohs scale of mineral hardness. Among the natural gems only moissanite and diamond are harder, with diamond having a Mohs hardness of 10.0 and moissonite falling somewhere in between corundum (ruby) and diamond in hardness.

All natural rubies have imperfections in them, including color impurities and inclusions of rutile needles known as "silk". Gemologists use these needle inclusions found in natural rubies to distinguish them from synthetics, simulants, or substitutes. Usually the rough stone is heated before cutting. Almost all rubies today are treated in some form, with heat treatment being the most common practice. However, rubies that are completely untreated but still of excellent quality command a large premium.

Some rubies show a 3-point or 6-point asterism or star. These rubies are cut into cabochons to display the effect properly. Asterisms are best visible with a single-light source, and move across the stone as the light moves or the stone is rotated. Such effects occur when light is reflected off the silk (the structurally oriented rutile needle. inclusions) in a certain way. This is one example where inclusions increase the value of a gemstone. Rubies can furthermore show color changes — though this occurs very rarely — and chatoyancy.

Natural Occurrence

Rubies are mined traditionaly in Myanmar (Burma), Siam (Thailand, and the Pailin and Samlot province of Cambodia) and Afghanistan. Rubies were rarely found in Sri Lanka where pink sapphires are more common. After the Second World War new ruby deposits were found in Tanzania, Kenya, Madagascar, Vietnam, Nepal, Tajikistan, and Pakistan. They have also been sometimes found in the states of Montana, North Carolina, and South Carolina. The Mogok Valley in Upper Myanmar was for centuries the world main source for rubies. It has produced some of the finest rubies ever mined, but in recent years very few good rubies have been found there. The very best color in Myanmar (Burmese) rubies is sometimes described as "pigeon’s blood". In central Myanmar the area of Mong Hsu also started to produces rubies during the 1990's and Mong Hsu became rapidly the world main ruby mining area. The latest ruby deposit to be found in Myanmar is situated in Namya (Namyazeik) located in the northern Kachin state. In 2002 rubies were found in the Waseges River area of Kenya. Spinel, another red gemstone, is sometimes found associated with rubies from the same gem gravel or marble. Red spinel may be mistaken with ruby by people lacking experience with gems. However, fine red spinels may approach the average ruby in value.

The value of natural rubies varies depending on their size, cut, origin, clarity and quality. As of 2000, a gem quality, uncut one carat (0.2 g) ruby cost about $4,200 USD. Since it is easy to spot synthetic rubies by their lack of natural inclusions, they have not greatly affected the price of natural rubies.

Treatments and Enhancements

Improving the quality of gemstones by treating them is common practice. Some treatments are used in almost all cases and are therefore considered acceptable. During the late 1990s, a large supply of low-cost materials caused a sudden surge in supply of heat-treated rubies, leading to a downward pressure on ruby prices.

Improvements used include color alteration, improving transparency by dissolving rutile inclusions, healing of fractures (cracks) or even completely filling them.

The most common treatment is the application of heat. Most if not all rubies at the lower end of the market are heat treated on the rough stones to improve color, remove purple tinge, blue patches and silk. These heat treatments typically occur around temperatures of 1800°C (3300°F). Some rubies undergo a process of low tube heat, when the stone is heated over charcoal of a temperature of about 1300°C (2400°F) for 20 to 30 minutes. The silk is only partially broken as the color is improved.

A less acceptable treatment, which has gained notoriety in recent years, is lead glass filling. Filling the fractures inside the ruby with lead glass dramatically improves the transparency of the stone, making previously unsuitable rubies fit for applications in jewelry. The process is done in four steps:

1. The rough stones are pre-polished to eradicate all surface impurities that may affect the process
2. The rough is cleaned with hydrogen fluoride
3. The first heating process during which no fillers are added. The heating process eradicates impurities inside the fractures. Although this can be done at temperatures up to 1400°C (2500°F) it most likely occurs at a temperature of around 900°C (1600°F) since the rutile silk is still intact
4. The second heating process in an electrical oven with different chemical additives. Different solutions and mixes have shown to be successful, however mostly lead-containing glass-powder is used at present. The ruby is dipped into oils, then covered with powder, embedded on a tile and placed in the oven where it is heated at around 900°C (1600°F) for one hour in an oxidizing atmosphere. The orange colored powder transforms upon heating into a transparent to yellow-colored paste, which fills all fractures. After cooling the color of the paste is fully transparent, that dramatically improves the overall transparency of the ruby.

If a color needs to be added, the glass powder can be "enhanced" with copper or other metal oxides as well as elements such as sodium, calcium, potassium etc.

The second heating process can be repeated three to four times, even applying different mixtures. When jewelry containing rubies is heated (for repairs) it should not be coated with boracic acid or any other substance, as this can etch the surface; it does not have to be "protected" like a diamond.